Nimonic 901 Tubes/Tubings (Nimonic Alloy 901, 2.4662, Alloy901)

• Type: Seamless
• Technique: Hot Rolled
• Material: Stainless Steel
• Surface Treatment: Polish
• Usage: Pipeline Transport
• Section Shape: Round
• Model NO.: jj246
• Certification: API, CE, UL
• Application: Boiler Pipe
• Material Grade of Pipes: Nimonic 901
• Transport Package: Bundle Packing with Woven Bag
• Specification: CE
• Trademark: LY
• Origin: Jiangyin
• HS Code: 722840000
• Production Capacity: 5000 Tons/Year

Product Description

We could produce Nimonic 901 seamless tubes, Nimonic901 seamless tube, Nimonic 901 tubings, Nimonic Alloy 901 seamless tube/welded tubes, Alloy901 seamless tube/welded tubes, 2.4662 seamless tube/welded tubes from china
The type of Nimonic 901, Nimonic Alloy901, 2.4662 tubes that we could do is as follows: U Bend Tubes, U-Tubes, forged tubes, forging tubes, coiled tubes, boiler tubes, heat exchanger tubes, Capillary tubes, Thermocouple tubes, Superheater tubes and reheater tubes, condenser tube, finned tubes, furnace tubes, instrumentation tubes, Evaporator tubes, honed tubes, Precision tubes, High pressure tubes, hydraulic tubes from china
The outer diameter of Nimonic 901, Nimonic Alloy901, 2.4662 tubes that we could do is from 0.4MM to 850MM, The thickness of Nimonic 901, Nimonic Alloy901, 2.4662 tubes that we could do is from 0.12MM to 100MM
As per surface finish of Nimonic 901, Nimonic Alloy901, 2.4662 tubes, we could do 180G, 320G Satin / Hairline(Matt Finish, Brush, Dull Finish), PICKLING surface finish as per the requirement of the clients
As per heat treatment of Nimonic 901, Nimonic Alloy901, 2.4662 tubes, we could do solution treatment, ageing treatment as per the requirement of the clients
Our Nimonic 901, Nimonic Alloy901, 2.4662 tubes/tubings are widely used in many industry like, Feed-water and steam generator tubing in power plants, Brine heaters and evaporator bodies in salt plants, Sulphuric and hydrouoric acid alkylation plants, Industrial heat exchangers, Cladding for crude oil distillation columns, Splash-zone sheathing in offshore structures, seawater service, Plants for isotope separation in the production of nuclear fuel pumps and valves used in the manufacture of chlorinated hydrocarbons and so on
We could supply Nimonic 901, Nimonic Alloy901, 2.4662 tubes/tubings material certificate as per En10204-3.1 or EN10204-3.2 by third parts(like TUV, DNV, GL, and so on)
Please send us the size and quantity of Nimonic 901, Nimonic Alloy901, 2.4662 tubes that you need, we are glad to quote the best price for your side

nimonic 901

nimonic 901 (UNS N09901/Din 1.4898)

nimonic 901 Chemical composition:

Alloy	%	Ni	Cu	Al	Fe	Ti	Co	Mn	S	C	Si	P	Cr	Mo	B
nimonic 901	Min.	40.0				2.35							11.0	5.0	0.01
	Max.	45.0	0.50	0.35	Balance	3.10	1.0	1.0	0.03	0.10	0.60	0.03	14.0	7.0	0.02

nimonic 901 Physical properties:

Density	8.14 g/cm3
Melting point	1280-1345ºC

nimonic 901 minimum mechanical properties in the room temperature:

Status	Tensile strength Rm N/mm2	Yield strength RP0.2N/mm2	Elongation A5 %
nimonic 901	1034	689	12

 

Description A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.

Corrosion Resistance Alloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.

Workability

Hot Working Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.

 

Weldability Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.