We are one leading producer of Nimonic 901 forged round bars, Nimonic 901 forging round bars, Nimonic901 forged/forging round bars, Nimonic Alloy 901 forging/forged round bars, Alloy901 forged/forging round bars, 2.4662 forging/forged round bars factory from china
We could produce Nimonic 901, Nimonic Alloy901, 2.4662 forging/forged round bars with diameters ranging from 10MM to 6000MM and with weights from 10KGS to 15000KGS
The melting method of Nimonic 901, Nimonic Alloy901, 2.4662 material is ESR+VIR or VIM+ESR+VAR
Our Nimonic 901, Nimonic Alloy901, 2.4662 forged/forging round bars are widely used in in chemical plants and heavy vessels, pump and valve producers, and industrial blades. Separators and centrifuges, Cement industry and sugar industry, drilling platform, drilling rig, pipelines and refineries, power generation and power plants, , generators, compressors, gear boxes. Oil & gas industry, concrete mills and mixers, processing units, crystalizer equipment and so on
Our Nimonic 901, Nimonic Alloy901, 2.4662 forged/forging round bars could be 100% Ultrasonic Inspection as per the forging parts UT Test standard of ASTM A 388 or EN10228.
We could supply Nimonic 901, Nimonic Alloy901, 2.4662 forged/forging round bars material certificate as per the standard of EN10204-3.1 or EN10204-3.2 of third party
Any inquiry of Nimonic 901, Nimonic Alloy901, 2.4662 forged/forging round bars, please feel free to contact us. We are glad to quote the best price for every clients
nimonic 901
nimonic 901 (UNS N09901/Din 1.4898)
nimonic 901 Chemical composition:
Alloy | % | Ni | Cu | Al | Fe | | Co | Mn | S | C | | P | Cr | Mo | B |
nimonic 901 | Min. | 40.0 | | | | 2.35 | | | | | | | 11.0 | 5.0 | 0.01 |
Max. | 45.0 | 0.50 | 0.35 | Balance | 3.10 | 1.0 | 1.0 | 0.03 | 0.10 | 0.60 | 0.03 | 14.0 | 7.0 | 0.02 |
nimonic 901 Physical properties:
Density | 8.14 g/cm3 |
Melting point | 1280-1345ºC |
nimonic 901 minimum mechanical properties in the room temperature:
Status | Tensile strength Rm N/mm2 | Yield strength RP0.2N/mm2 | Elongation A5 % |
nimonic 901 | 1034 | 689 | 12 |
Description A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.
Corrosion Resistance Alloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.
Workability
Hot Working Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.
Weldability Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.