Nimonic 901 Forged/Forging Shafts (Nimonic Alloy 901, 2.4662, Alloy901)

• Processing Object: Non-Metallic
• Molding Style: Forging
• Molding Technics: Forging
• Application: Machinery Parts
• Material: SS
• Heat Treatment: Quenching
• Model NO.: jj244
• Surface Treatment: Polishing
• Forging Tolerance: +/-0.5mm
• Standard: AISI
• Certification: SGS
• Material of Forged Shafts: Nimonic 901
• Transport Package: Wooden or Steel Frame Crate Packing
• Specification: CE
• Trademark: LY
• Origin: Jiangyin
• HS Code: 722840000
• Production Capacity: 5000 Tons/Year

Product Description

We are one leading producer of Nimonic 901 forged shafts, Nimonic 901 forging shafts, Nimonic901 forged/forging shafts, Nimonic Alloy 901 forged/forging shafts, Alloy901 forging/forged shafts, 2.4662 forged/forging shafts factory from china.
We could produce Nimonic 901, Nimonic Alloy901, 2.4662 forged/forging shafts with diameters ranging from 100MM to 1200MM, with length from 100MM to 10000MM, the weight from 10KGS to 15000KGSs
We could do rough or final machined of Nimonic 901, Nimonic Alloy901, 2.4662 forged/forging shaft as per the drawing of the clients
The type of Nimonic 901, Nimonic Alloy901, 2.4662 forged/fortging shafts that we could do is as follows: Forged eccentric shafts, forged crank shafts, forged pump shafts, forged generator shafts, forging shipping shafts and so on
Our Nimonic 901, Nimonic Alloy901, 2.4662 forged/fortging shafts are widely used in chemical pump, centrifugal pumps, High Pressure Pump, Plunger pump. Mud pump, Fracturing Pump. Cement industry and sugar industry, paper mills. Off-highway. Shipping building and Aviation, power generation and power plants, in oil & gas industry, concrete mills and mixers, processing units, mechanical equipment.
Our Nimonic 901, Nimonic Alloy901, 2.4662 forged/fortging shafts could be 100% Ultrasonic Inspection as per the forging parts UT Test standard of ASTM A 388 or EN10228.
We could supply Nimonic 901, Nimonic Alloy901, 2.4662 forged/fortging shafts material certificate as per the standard of EN10204-3.1 or EN10204-3.2 of third party
Any inquiry of Nimonic 901, Nimonic Alloy901, 2.4662 forged/fortging shafts, please feel free to contact us. We are glad to quote the best price for every clients

nimonic 901

nimonic 901 (UNS N09901/Din 1.4898)

nimonic 901 Chemical composition:

Alloy	%	Ni	Cu	Al	Fe	Ti	Co	Mn	S	C	Si	P	Cr	Mo	B
nimonic 901	Min.	40.0				2.35							11.0	5.0	0.01
	Max.	45.0	0.50	0.35	Balance	3.10	1.0	1.0	0.03	0.10	0.60	0.03	14.0	7.0	0.02

nimonic 901 Physical properties:

Density	8.14 g/cm3
Melting point	1280-1345ºC

nimonic 901 minimum mechanical properties in the room temperature:

Status	Tensile strength Rm N/mm2	Yield strength RP0.2N/mm2	Elongation A5 %
nimonic 901	1034	689	12

 

Description A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.

Corrosion Resistance Alloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.

Workability

Hot Working Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.

 

Weldability Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.