We are one leading producer of HAYNES HR-160 forged round bars, HAYNES HR-160 forging round bars, UNS N12160 forging/forged round bars, HAYNES HR160 forged/forging round bars, 2.4880 forging/forged round bars factory from china
We could produce HAYNES HR-160, UNS N12160, 2.4880 forging/forged round bars with diameters ranging from 10MM to 6000MM and with weights from 10KGS to 15000KGS
The melting method of HAYNES HR-160, UNS N12160, 2.4880 material is ESR+VIR or VIM+ESR+VAR
Our HAYNES HR-160, UNS N12160, 2.4880 forged/forging round bars are widely used in in chemical plants and heavy vessels, pump and valve producers, and industrial blades. Separators and centrifuges, Cement industry and sugar industry, drilling platform, drilling rig, pipelines and refineries, power generation and power plants, , generators, compressors, gear boxes. Oil & gas industry, concrete mills and mixers, processing units, crystalizer equipment and so on
Our HAYNES HR-160, UNS N12160, 2.4880 forged/forging round bars could be 100% Ultrasonic Inspection as per the forging parts UT Test standard of ASTM A 388 or EN10228.
We could supply HAYNES HR-160, UNS N12160, 2.4880 forged/forging round bars material certificate as per the standard of EN10204-3.1 or EN10204-3.2 of third party
Any inquiry of HAYNES HR-160, UNS N12160, 2.4880 forged/forging round bars, please feel free to contact us. We are glad to quote the best price for every clients
The chemical composition of HAYNES HR-160 bars is as follows
|
Nominal Chemical Composition, Weight Percent |
|
Ni |
Co |
Cr |
Fe |
Si |
Mn |
Ti |
C |
W |
Mo |
Cb |
|
|
|
37a |
29 |
28 |
2* |
2.75 |
0.5 |
0.5 |
0.05 |
1* |
1* |
1* |
|
aAs Balance *Maximum |
|
The mechanical property of HAYNES HR160 bars is as follows
|
Test
Temperature |
Ultimate Tensile Strength |
Yield Strength
at 0.2% Offset |
Elongation in 1.340 in. (34.0 mm) |
Reduction
of Area |
|
|
|
°F |
(°C) |
Ksi |
MPa |
Ksi |
MPa |
% |
% |
|
|
|
70 |
(21) |
111.2 |
767 |
45.6 |
314 |
68 |
73 |
|