Incoloy 901 Seamless Pipes/Welded Pipes (UNS N09901, 1.4898, Alloy 901)

• Type: Seamless
• Technique: Hot Rolled
• Surface Treatment: Polish
• Usage: Pipeline Transport
• Section Shape: Round
• Certification: API, CE, UL
• Model NO.: jj235
• Application: Boiler Pipe
• Material Grade of Seamless Pipes: Incoloy 901
• Transport Package: Bundle and Wooden Box Packing
• Specification: CE
• Trademark: LY
• Origin: Jiangyin
• HS Code: 722840000
• Production Capacity: 5000 Tons/Year

Product Description

We could produce Incoloy 901 seamless pipes, Incoloy901 seamless pipe, UNS N09901 seamless pipe/welded pipes, Alloy 901 seamless pipe/welded pipes, 1.4898 seamless pipe/welded pipes from china
The type of Incoloy 901, UNS N09901, 1.4898 pipes that we could do is as follows: Forged pipes, forging pipes, coiled pipes, boiler pipes, heat exchanger pipes, Capillary pipes, Thermocouple pipes, Superheater pipes and reheater pipes, condenser pipe, finned pipes, furnace pipes, instrumentation pipes, Evaporator pipes, honed pipes, Precision pipes, High pressure pipes, hydraulic pipes and so on
The outer diameter of Incoloy 901, UNS N09901, 1.4898 pipes that we could do is from 0.4MM to 850MM, The thickness of Incoloy 901, UNS N09901, 1.4898 pipes that we could do is from 0.12MM to 100MM
We could do pickled and polish into bright surface as per the requirement of the clients, also for bright surface of Incoloy 901, UNS N09901, 1.4898 pipes, we could meet 2D finish. No. 4 Finish, No. 6 Finish, No. 7 Finish as per the requirement of the clients
We will do Positive material identification (PMI), Visual inspection, Dimensional inspection. Laser micrometer inspection, Destructive testing( includes tensile, hardness, bending, flattening, flare and metallurgical tests), ultrasonic testing and pressure testing, Liquid Penetrate testing as per the requirement of the clients to control the quality of Incoloy 901, UNS N09901, 1.4898 pipes
Please send us the size and quantity of Incoloy 901, UNS N09901, 1.4898 pipes that you need, we are glad to quote the best price for your side

 Chemical composition:
 

Alloy	%	Ni	Cu	Al	Fe	Ti	Co	Mn	S	C	Si	P	Cr	Mo	B
N09901	Min.	40.0			Balance	2.35							11.0	5.0	0.01
	Max.	45.0	0.50	0.35		3.10	1.0	1.0	0.03	0.10	0.60	0.03	14.0	7.0	0.02

 

 Physical properties:
 

Density	8.14 g/cm3
Melting point	1280-1345°C

 

 Minimum mechanical properties in the room temperature:
 

Status	Tensile strength Rm N/mm2	Yield strength RP0.2 N/mm2	Elongation A5 %
N09901	1034	689	12

 
Description

A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.

Corrosion Resistance
It has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.

Workability
 
Hot Working
It is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.
 
Weldability
It can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.