We are one leading producer of 904L forged shafts, 904L forging shafts, 904 L forged/forging shafts, UNS N08904 forged/forging shafts, Alloy 904 L forging/forged shafts, 1.4539 forged/forging shafts factory from china.
We could produce 904L, UNS N08904, 1.4539 forged/forging shafts with diameters ranging from 100MM to 1200MM, with length from 100MM to 10000MM, the weight from 10KGS to 15000KGSs
We could do rough or final machined of 904L, UNS N08904, 1.4539 forged/forging shaft as per the drawing of the clients
The type of 904L, UNS N08904, 1.4539 forged/fortging shafts that we could do is as follows: Forged eccentric shafts, forged crank shafts, forged pump shafts, forged generator shafts, forging shipping shafts and so on
Our 904L, UNS N08904, 1.4539 forged/fortging shafts are widely used in chemical pump, centrifugal pumps, High Pressure Pump, Plunger pump. Mud pump, Fracturing Pump. Cement industry and sugar industry, paper mills. Off-highway. Shipping building and Aviation, power generation and power plants, in oil & gas industry, concrete mills and mixers, processing units, mechanical equipment.
Our 904L, UNS N08904, 1.4539 forged/fortging shafts could be 100% Ultrasonic Inspection as per the forging parts UT Test standard of ASTM A 388 or EN10228.
We could supply 904L, UNS N08904, 1.4539 forged/fortging shafts material certificate as per the standard of EN10204-3.1 or EN10204-3.2 of third party
Any inquiry of 904L, UNS N08904, 1.4539 forged/fortging shafts, please feel free to contact us. We are glad to quote the best price for every clients
Grade 904L stainless steel is a non-stabilized austenitic stainless steel with low carbon content. This high alloy stainless steel is added with copper to improve its resistance to strong reducing acids, such as sulphuric acid. The steel is also resistant to stress corrosion cracking and crevice corrosion. Grade 904L is non-magnetic, and offers excellent formability, toughness and weldability.
Grade 904L contains high amounts of expensive ingredients, such as molybdenum and nickel. Today, most of the applications that employ grade 904L are replaced by low-cost duplex stainless steel 2205.
Composition
The table below provides the compositional ranges of grade 904L stainless steels:
Table 1. Composition ranges of grade 904L stainless steels
Chemical Formula
Fe, <0.02% C, 19-23% Cr, 23-28% Ni, 4-5% Mo, <2.0% Mn, <1.0% Si, <0.045% P, <0.035% S, 1.0-2.0% Cu
Mechanical Properties
Table 2. Mechanical properties of grade 904L stainless steels
Grade |
Tensile Strength (MPa) min |
Yield Strength 0.2% Proof (MPa) min |
Elongation (% in 50mm) min |
Hardness |
| Rockwell B (HR B) |
Brinell (HB) |
| 904L |
490 |
220 |
36 |
70-90 typical |
150 |
Physical Properties
Table 3. Typical physical properties of grade 904L stainless steels
Grade |
Density |
Elastic Modulus |
Mean Co-eff of Thermal Expansion (µm/m/°C) |
Thermal Conductivity |
Specific Heat 0-100°C |
Elec Resistivity |
| (kg/m3) |
(GPa) |
(W/m.K) |
(J/kg.K) |
(nΩ.m) |
| |
|
0-100°C |
0-315°C |
0-538°C |
At 20°C |
At 500°C |
|
|
| 904L |
7900 |
190 |
15 |
- |
- |
11.5 |
- |
500 |
952 |
Corrosion Resistance
Grade 904L stainless steels have excellent resistance to warm seawater and chloride attack. The high resistance of grade 904L against stress corrosion cracking is due to the presence of high amounts of nickel in its composition. Moreover, the addition of copper to these grades develops resistance to sulphuric acid and other reducing agents in both aggressive and mild conditions.
The corrosion resistance of grade 904L is intermediate between super austenitic grades, with 6% molybdenum content, and standard 316L austenitic grades. Grade 904L is less resistant to nitric acid than grades 304L and 310L, which are free of molybdenum. This steel grade needs to be solution treated following cold working, to achieve maximum stress corrosion cracking resistance under critical environments.
Heat Resistance
Grade 904L stainless steels offer good oxidation resistance. However, the structural stability of this grade collapses at high temperatures, particularly above 400°C.
Heat Treatment
Grade 904L stainless steels can be solution heat-treated at 1090 to 1175°C, following by rapid cooling. Thermal treatment is suitable for hardening these grades.
Welding
Welding of grade 904L stainless steels can be performed using all conventional methods. This grade does not require pre-heat and post-weld heat treatments. Grade 904L can be subjected to hot cracking in constrained weldment. Grade 904L electrodes and rods are used for welding grade 904L steels according to AS 1554.6.
Fabrication
Grade 904L stainless steels are high purity steels with low sulphur content. They can be machined using any standard methods. These grades can be readily bent to a small radius under cold conditions. Although subsequent annealing is not required in most cases, it should be carried out when the fabrication is performed under severe stress corrosion cracking conditions.