We produce AISI 321H Plates, Sheets, Coils, Strips, UNS S32109 Plates, Sheets, Coils, Strips, 1.4940 Plates, Sheets, Coils, Strips, AISI 321 H Plates, Sheets, Coils, Strips from china
We could produce AISI 321H, UNS S32109, 1.4940 Plates/Sheets/Coils/Strips with Sizes range from 4.5MM thick to 200MM thickness, up to 3000 wide.
The thickness of AISI 321H, UNS S32109, 1.4940 Plates/Sheets/Coils/Strips that we could do range from 0.05MM to 3MM
The surface finish of AISI 321H, UNS S32109, 1.4940 Plates/Sheets/Coils/Strips that we could do is as follows: 2B / 2D / BA
The hardness of AISI 321H, UNS S32109, 1.4940 Plates/Sheets/Coils/Strips that we could do is as follows: 1/4 Hard, 1/2 Hard, 3/4 Hard, Full Hard, Spring Hard, Annealed, Pickled Soft
We can polish AISI 321H, UNS S32109, 1.4940 Plates/Sheets/Coils/Strips to a #4 polish, #6 Polish, #7 polish or a #8 mirror finish. Our AISI 321H, UNS S32109, 1.4940 plate, sheets, coils, strips can be polished on one side or two sides.
Our AISI 321H, UNS S32109, 1.4940 Plates/Sheets/Coils/Strips are widely used in Chemical industry, Aerospace, Heat treating industry, Pulp and paper industry, Food processing, Nuclear Engineering, Gas turbine components and so on.
Please tell us the size of AISI 321H, UNS S32109, 1.4940 Plates/Sheets/Coils/Strips that you need, we are glad to quote the best price
321H is a general purpose austenitic stainless steel that is stabilized against carbide precipitation and designed to work within the carbide precipitation temperature range 427 to 816°C (800 to 1500°F)
The chemical composition of 321H bars is as follows
Element |
Content (%) |
Iron, Fe |
Balance |
Chromium, Cr |
17-19 |
Nickel, Ni |
9-12 |
Manganese, Mn |
2 |
Silicon, Si |
1 |
Titanium, Ti |
0.35 |
Phosphorous, P |
0.045 |
Carbon, C |
0.04-0.10 |
Sulfur, S |
0.03 |
The mechanical property of 321 H bars is as follows
Properties |
Metric |
Imperial |
Tensile strength |
480 MPa |
69600 psi |
Yield strength |
205 MPa |
29700 ksi |
Elongation at break |
29% |
29% |
Hardness, Brinell |
≤187 |
≤187
|