We produce Hastelloy B Plates, Sheets, Coils, Strips, UNS N10001 Plates, Sheets, Coils, Strips, 2.4810 Plates, Sheets, Coils, Strips, Alloy B Plates, Sheets, Coils, Strips from china
We could produce Hastelloy B, UNS N10001, 2.4810 Plates/Sheets/Coils/Strips with Sizes range from 4.5MM thick to 200MM thickness, up to 3000 wide.
The thickness of Hastelloy B, UNS N10001, 2.4810 Plates/Sheets/Coils/Strips that we could do range from 0.05MM to 3MM
The surface finish of Hastelloy B, UNS N10001, 2.4810 Plates/Sheets/Coils/Strips that we could do is as follows: 2B / 2D / BA
The hardness of Hastelloy B, UNS N10001, 2.4810 Plates/Sheets/Coils/Strips that we could do is as follows: 1/4 Hard, 1/2 Hard, 3/4 Hard, Full Hard, Spring Hard, Annealed, Pickled Soft
We can polish Hastelloy B, UNS N10001, 2.4810 Plates/Sheets/Coils/Strips to a #4 polish, #6 Polish, #7 polish or a #8 mirror finish. Our Hastelloy B, UNS N10001, 2.4810 plate, sheets, coils, strips can be polished on one side or two sides.
Our Hastelloy B, UNS N10001, 2.4810 Plates/Sheets/Coils/Strips are widely used in Chemical industry, Aerospace, Heat treating industry, Pulp and paper industry, Food processing, Nuclear Engineering, Gas turbine components and so on.
Please tell us the size of Hastelloy B, UNS N10001, 2.4810 Plates/Sheets/Coils/Strips that you need, we are glad to quote the best price
UNS N10001
Form |
ASTM |
| Rod |
B 335 |
| Plate, sheet and strip |
B 333, B 906 |
| Seamless pipe and tube |
B 622 |
| Welded pipe |
B 619, B 775 |
| Welded tube |
B 626, B 751 |
| Welding fitting |
B 366 |
Chemical composition
% |
Ni |
Mo |
Fe |
Co |
Cr |
C |
Mn |
Si |
P |
S |
V |
| min |
balance |
26.0 |
4.0 |
|
|
|
|
|
|
|
0.20 |
| max |
30.0 |
6.0 |
2.5 |
1.00 |
0.050 |
1.00 |
1.00 |
0.040 |
0.030 |
0.40 |
Physical properties
Density |
9.24 g/cm3 |
| Melting range |
1330-1380°C |
Features: Hastelloy B has excellent resistance to reducing environments like sulfuric acid at moderate concentrations and other nonoxidizing acids. It also resists stress corrosion cracking induced by chlorides. Hastelloy B has poor resistance to oxidizing environments, therefore, it should not be used where ferric or cupric salts are present as these salts may cause rapid corrosion failure.
Applications: Equipment handling reducing chemical environments; and chemical process industry involving hydrochloric, sulfuric, phosphoric and acetic acids.