Nimonic 901 Plates/Sheets/Coils/Strips (Nimonic Alloy 901, 2.4662, Alloy901)

• Customization: Available
• Type: Steel Plate
• Standard: ASTM, JIS, DIN
• Model NO.: jj248
• Surface Treatment: Polish
• Technique: Hot Rolled
• Application: Boiler Plate
• Special Use: Wear Resistant Steel
• Stock: Stock
• Material of Plates: Nimonic 901
• Transport Package: Bundle Packing with Woven Bag
• Specification: CE
• Trademark: LY
• Origin: Jiangyin
• HS Code: 722840000
• Production Capacity: 5000 Tons/Year

Product Description

We produce Nimonic 901, Nimonic901 Plates, Sheets, Coils, Strips, Nimonic Alloy 901 Plates, Sheets, Coils, Strips, 2.4662 Plates, Sheets, Coils, Strips, Alloy901 Plates, Sheets, Coils, Strips from china
We could produce Nimonic 901, Nimonic Alloy901, 2.4662 Plates/Sheets/Coils/Strips with Sizes range from 4.5MM thick to 200MM thickness, up to 3000 wide.
The thickness of Nimonic 901, Nimonic Alloy901, 2.4662 Plates/Sheets/Coils/Strips that we could do range from 0.05MM to 3MM
The surface finish of Nimonic 901, Nimonic Alloy901, 2.4662 Plates/Sheets/Coils/Strips that we could do is as follows: 2B / 2D / BA
The hardness of Nimonic 901, Nimonic Alloy901, 2.4662 Plates/Sheets/Coils/Strips that we could do is as follows: 1/4 Hard, 1/2 Hard, 3/4 Hard, Full Hard, Spring Hard, Annealed, Pickled Soft
We can polish Nimonic 901, Nimonic Alloy901, 2.4662 Plates/Sheets/Coils/Strips to a #4 polish, #6 Polish, #7 polish or a #8 mirror finish. Our Nimonic 901, Nimonic Alloy901, 2.4662 plate, sheets, coils, strips can be polished on one side or two sides.
Our Nimonic 901, Nimonic Alloy901, 2.4662 Plates/Sheets/Coils/Strips are widely used in Chemical industry, Aerospace, Heat treating industry, Pulp and paper industry, Food processing, Nuclear Engineering, Gas turbine components and so on.
Please tell us the size of Nimonic 901, Nimonic Alloy901, 2.4662 Plates/Sheets/Coils/Strips that you need, we are glad to quote the best price

nimonic 901

nimonic 901 (UNS N09901/Din 1.4898)

nimonic 901 Chemical composition:

Alloy	%	Ni	Cu	Al	Fe	Ti	Co	Mn	S	C	Si	P	Cr	Mo	B
nimonic 901	Min.	40.0				2.35							11.0	5.0	0.01
	Max.	45.0	0.50	0.35	Balance	3.10	1.0	1.0	0.03	0.10	0.60	0.03	14.0	7.0	0.02

nimonic 901 Physical properties:

Density	8.14 g/cm3
Melting point	1280-1345ºC

nimonic 901 minimum mechanical properties in the room temperature:

Status	Tensile strength Rm N/mm2	Yield strength RP0.2N/mm2	Elongation A5 %
nimonic 901	1034	689	12

 

Description A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.

Corrosion Resistance Alloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.

Workability

Hot Working Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.

 

Weldability Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.