We could produce Nimonic 901 seamless pipes, Nimonic901 seamless pipe, Nimonic Alloy 901 seamless pipe/welded pipes, Alloy901 seamless pipe/welded pipes, 2.4662 seamless pipe/welded pipes from china
The type of Nimonic 901, Nimonic Alloy901, 2.4662 pipes that we could do is as follows: Forged pipes, forging pipes, coiled pipes, boiler pipes, heat exchanger pipes, Capillary pipes, Thermocouple pipes, Superheater pipes and reheater pipes, condenser pipe, finned pipes, furnace pipes, instrumentation pipes, Evaporator pipes, honed pipes, Precision pipes, High pressure pipes, hydraulic pipes and so on
The outer diameter of Nimonic 901, Nimonic Alloy901, 2.4662 pipes that we could do is from 0.4MM to 850MM, The thickness of Nimonic 901, Nimonic Alloy901, 2.4662 pipes that we could do is from 0.12MM to 100MM
We could do pickled and polish into bright surface as per the requirement of the clients, also for bright surface of Nimonic 901, Nimonic Alloy901, 2.4662 pipes, we could meet 2D finish. No. 4 Finish, No. 6 Finish, No. 7 Finish as per the requirement of the clients
We will do Positive material identification (PMI), Visual inspection, Dimensional inspection. Laser micrometer inspection, Destructive testing( includes tensile, hardness, bending, flattening, flare and metallurgical tests), ultrasonic testing and pressure testing, Liquid Penetrate testing as per the requirement of the clients to control the quality of Nimonic 901, Nimonic Alloy901, 2.4662 pipes
Please send us the size and quantity of Nimonic 901, Nimonic Alloy901, 2.4662 pipes that you need, we are glad to quote the best price for your side
nimonic 901
nimonic 901 (UNS N09901/Din 1.4898)
nimonic 901 Chemical composition:
Alloy |
% |
Ni |
Cu |
Al |
Fe |
Ti |
Co |
Mn |
S |
C |
Si |
P |
Cr |
Mo |
B |
nimonic 901 |
Min. |
40.0 |
|
|
|
2.35 |
|
|
|
|
|
|
11.0 |
5.0 |
0.01 |
Max. |
45.0 |
0.50 |
0.35 |
Balance |
3.10 |
1.0 |
1.0 |
0.03 |
0.10 |
0.60 |
0.03 |
14.0 |
7.0 |
0.02 |
nimonic 901 Physical properties:
Density |
8.14 g/cm3 |
Melting point |
1280-1345ºC |
nimonic 901 minimum mechanical properties in the room temperature:
Status |
Tensile strength Rm N/mm2 |
Yield strength
RP0.2N/mm2 |
Elongation
A5 % |
nimonic 901 |
1034 |
689 |
12 |
Description A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.
Corrosion Resistance Alloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.
Workability
Hot Working Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.
Weldability Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.