We are leading producer of Incoloy 901 forged Parts/pipes/tubes/sleeves/bushings, Incoloy 901 forging Parts/pipes/tubes/sleeves/bushings, Incoloy901 forging/forged Parts/pipes/tubes/sleeves/bushings, alloy 901 forging/forged Parts/pipes/tubes/sleeves/bushings, UNS N09901 forged/forging Parts/pipes/tubes/sleeves/bushings, 1.4898 forging/forged Parts/pipes/tubes/sleeves/bushings factory from China.
We could produce Incoloy 901, UNS N09901, 1.4898 forged/forging Parts/pipes/tubes/sleeves/bushings with diameters ranging from 50MM to 6000MM and with weights from 10KGS to 15000KGS
We have 1 tons, 3 tons, 6 tons, 9 tons forging hammer and 4500 tons hydraulic press, and 3 metres and 6 metre seamless rolled rings machine to make forging of Incoloy 901 UNS N09901, 1.4898
We could do solution treatment and ageing treatment for Incoloy 901 UNS N09901, 1.4898 forging/forged parts as per the clients
Our Incoloy 901, UNS N09901, 1.4898 forging/forged Parts/pipes/tubes/sleeves/bushings are widely used in petroleum and chemical industry, power generation, shipbuilding, heavy machinery, Oil&Gas applications: Such as christmas trees, wellhead components, spools, valves, BOP's, riser application, nozzles, pressure vessel, Y-blocks and so on
The type of Incoloy 901, UNS N09901, 1.4898 forging/forged parts that we could do is as follows: Forged shaft, forged roun bars, forged flanges, forging disks, forged tube sheets, forged gears, forged pipes, forged sleeves, forged blocks, forged rings, rolled rings, forged blocks and so on
Any inquiry of Incoloy 901 UNS N09901, 1.4898 forging/forged parts, please feel free to contact us. We are glad to quote the best price for every clients
Chemical composition:
Alloy |
% |
Ni |
Cu |
Al |
Fe |
Ti |
Co |
Mn |
S |
C |
Si |
P |
Cr |
Mo |
B |
N09901 |
Min. |
40.0 |
|
|
Balance |
2.35 |
|
|
|
|
|
|
11.0 |
5.0 |
0.01 |
Max. |
45.0 |
0.50 |
0.35 |
3.10 |
1.0 |
1.0 |
0.03 |
0.10 |
0.60 |
0.03 |
14.0 |
7.0 |
0.02 |
Physical properties:
Density |
8.14 g/cm3 |
Melting point |
1280-1345°C |
Minimum mechanical properties in the room temperature:
Status |
Tensile strength Rm
N/mm2 |
Yield strength RP0.2
N/mm2 |
Elongation A5
% |
N09901 |
1034 |
689 |
12 |
Description
A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.
Corrosion Resistance
It has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.
Workability
Hot Working
It is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.
Weldability
It can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.